MPP-A80E
Data Sheet
This high performance polyether system is one of a family of polymer systems developed by Northstar Polymers for specific demanding work environments. Urethane elastomers molded with this system exhibit fine resolution of mold details, good performance in wet environments and good resistance to ultraviolet light. This combination of features makes elastomers molded from MPP-A80E perfect for applications including patterns designed to transfer an image to wet surfaces including concrete and many custom applications.
Typical Physical Properties
Physical Property
ASTM #
Typical Value
Durometer Hardness:
D 2240
A80
Modulus (psi):
100% Elongation:
D 412
763
Tensile Strength (psi):
D 412
1113
Ultimate Elongation (%):
D 412
177
Tear Resistance (pli)
Die C:
D 624
140
Split:
D 624
25
Taber Abrasion (mg loss):
D 4060
28
Bashore Rebound (%):
D 2632
32
Typical Processing Conditions
Prepolymer:
MPN-023
Curing Agent:
PBA-031
Catalyst:
Included
Prepolymer Temperature (ºF):
Room Temperature**
Curing Agent Temperature (ºF):
Room Temperature**
Mold Temperature (ºF):
Room Temperature**
Pot Life*(minutes):
10 - 15
De-mold Time*** at 77ºF (hours):
5 - 6
Complete Cure Cycle*** at 77 °F (hours):
24
* Defined as: a 300 gram sample is too thick to pour.
** Between 70 ºF and 90 ºF. Higher temperature results faster curing pattern
*** The use of catalyst or higher mold temperature will increase the rate of cure. Mold may needed to be heated to 100 - 120 ºF for casting a very thin layer and/or using a heat-absorbing material for mold or inserts.
Typical Mixing Ratio
Prepolymer (A) Curing Agent (B)
Code Number: MPN-023 PBA-031
Specific Gravity: 1.173 1.026
Equivalent Weight: 226 308
Stoichiometry: 1.00 0.96
NCO/OH Index: 1.04 1.00
Weight Pph: 43.2 56.8
Weight Ratio: 1.000 1.312
Weight Ratio: 0.762 1.000
Volume Pph: 40.0 60.0
Volume Ratio: 1.000 1.500
Volume Ratio: 0.667 1.000
The actual mixing ratio at the operation may need to be adjusted based on the actual stoichiometric ratio calculation. For machine mixing, the mixing ratio calibration is recommended before the new batch of raw material is used.
Northstar Polymers, LLC
3444 Dight Avenue South
Minneapolis, MN 55406
Tel: 612.721.2911
Fax: 612.721.1009
E-Mail: info@northstarpolymers.com
Notice: All of the statements, recommendations, suggestions, and data concerning the subject material are based on our laboratory results, and although we believe the same to be reliable, we expressly do not represent, warrant, or guarantee the accuracy, completeness, or reliability of same, or the material or the results to be obtained from the use thereof, neither do we warrant that any such use, either alone or in combination with other materials, shall be free of the rightful claim of any third party by way of INFRINGEMENT or the like, and NORTHSTAR POLYMERS DISCLAIMS ALL WARRANTIES, EXPRESS OR IMPLIED, OF MERCHANTABILITY and FITNESS FOR A PARTICULAR PURPOSE.